Microstructure evolution and mechanical properties of refractory Mo-Nb-V-W-Ti high-entropy alloys

Abstract

High-entropy alloys can either be defined as solid solution alloys containing at least five elements in equiatomic or near-equiatomic composition, or as alloys with high configurational entropies (larger than 1.5R), regardless of the number of elements involved. The present study reports on an alloy design route for refractory high-entropy alloys based on equiatomic Mo-Nb-V alloys with additions of W and Ti. In general, the work was motivated by Senkov et al. The aim of the experiments carried out was to produce a refractory high-entropy alloy with a single-phase structure. For this purpose, a systematic alloy design involving four- and five-element compositions was used. Scanning electron microscopy analysis has shown that Mo-Nb-V-xW-yTi (x = 0, 20; y = 5, 10, 15, 20, 25) is in fact a refractory high-entropy alloy with a body-centered cubic dendritic structure. Furthermore, the Ti-concentration of the experimental alloys was varied, to obtain the influence of Titanium on the microstructure development. Additionally, compressive tests at room temperature were carried out to evaluate the influence of the di erent alloying elements and the Ti-fraction on the mechanical properties. The observations of the present work are then compared to the published results on similar alloys from the working group of Yao et al. and critically discussed.