Title: Multicrystalline, highly oriented thick-film silicon from reduction of soda-lime glass
Author(s): Schall, Ingrid
Ebbinghaus, StefanLook up in the Integrated Authority File of the German National Library
Strelow, ChristianLook up in the Integrated Authority File of the German National Library
Peiner, ErwinLook up in the Integrated Authority File of the German National Library
Issue Date: 2023
Type: Article
Language: English
Abstract: The study describes synthesis and characterization of > 10 µm thick multicrystalline (mc), highly oriented, p-doped silicon layers by aluminothermic reduction of low-cost soda-lime glass. X-ray diffraction shows a highly preferred (111)-orientation and excellent crystallinity. Low compressive stress and very good crystallinity are confirmed by the peak position and width of the Raman LO-phonon line, approaching the one of bulk single-crystalline wafer material. Due to strong bonding to the glass substrate layer, spalling is not observed. A conductive aluminum-rich oxide layer is formed underneath the silicon, serving as an electrical back-contact for electronic devices. Using secondary ion mass spectrometry very low concentrations of 1014–1015 cm−3 of impurities are found originating from the soda-lime glass with an iron content below the detection limit. Furthermore, a plateau-like, very homogenous Al concentration of ≈4 × 1018 cm−3 over a thickness of ≈10 µm is found, which corresponds to the solubility of Al in Si at the process temperature. Complete electronic activation within the plateau region is confirmed by carrier concentration measurements using electrochemical capacitance–voltage profiling and Raman spectroscopy. Hole concentrations in the range of few 1018 cm−3 are beneficial for the p-type base material of full-emitter cell mc-silicon photovoltaic devices.
Open Access: Open access publication
License: (CC BY 4.0) Creative Commons Attribution 4.0(CC BY 4.0) Creative Commons Attribution 4.0
Journal Title: Advanced materials interfaces
Publisher: Wiley-VCH
Publisher Place: Weinheim
Volume: 10
Issue: 35
Original Publication: 10.1002/admi.202300681
Page Start: 1
Page End: 9
Appears in Collections:Open Access Publikationen der MLU